Formlabs Grey Pro Resin

Grey Pro Resin

Grey Pro Resin is a tough, heat-resistant material with low creep, offering higher elongation and toughness than Formlabs standard resins.

This versatile material is suitable for concept modeling, appearance prototypes, and functional prototypes that require rigorous real-world testing.

Grey Pro Resin is compatible with Form 2 and Form 3 series printers. On the Form 4 series, Grey Resin V5 replaces Grey Pro Resin, offering improved mechanical properties and triple the print speed.

*If in stock, product will be delivered within 3 days of ordering. If out of stock, delivery will take place within 3 days after restocking.

Production Description
Features

Grey Pro Resin 1L

Grey Pro Resin is a high-precision, medium-elongation, and low-creep material. It’s an excellent choice for concept modeling and functional prototyping, especially for reusable parts.

Applications:
* Form and fit testing
* Injection-molded product prototypes
* Plastic, silicone, and other mold prototypes
* Jigs and fixtures

Jig System Setup

Full Line of Formlabs Resins

Grey Pro Resin Printed Assembly Part

物性表

樹脂	灰色Pro樹脂
	公制		英制
測試項目	素模	固化後	素模	固化後	方法
Tensile Properties 拉伸性能
Ultimate Tensile Strength 極限抗拉強度	35 MPa	61 MPa	5076 psi	8876 psi	ASTM D 638-14
Tensile Modulus拉伸模量	1.4 GPa	2.6 GPa	203 ksi	377 ksi	ASTM D 638-14
Elongation伸長	32.5 %	13 %	32.5 %	13 %	ASTM D 638-14
Flexural Stress at 5% Strain 5%應變下的彎曲強度	39 MPa	86 MPa	5598 psi	12400 psi	ASTM D 790-15
Flexural Modulus彎曲係數	0.94 GPa	2.2 GPa	136 ksi	319 ksi	ASTM D 790-15
Notched IZOD耐衝擊強度	未測試	18.7 J/m	未測試	0.351 ft-lbf/in	ASTM D256-10
Head Deflection Temp. @ 1.8 MPa 熱變型溫度	未測試	62.4 C	未測試	144.3 °F	ASTM D 648-16
Heat Deflection Temp. @ 0.45 MPa 熱變型溫度	未測試	77.5 C	未測試	171.5 °F	ASTM D 648-16
Thermal Expansion (-30 to 30° C) 熱膨脹	未測試	78.5 um/m/C	未測試	43.4 μin/in/°F	ASTM E 831-13

註:
1.列印機型：Form2，層厚度設定：0.1mm
2.光固條件: Form Cure 120分鐘/80℃
3.材料屬性可能因物件幾何形狀、列印方向，列印設定和溫度而異。

Mechanical Propertie 機械性能	24 hr weight gain (%) 24小時增加重量比	Mechanical Properties 機械性能	24 hr weight gain (%) 24小時增加重量比
Acetic Acid, 5 % 乙酸	0.75	Water 水	0.83
Acetone 丙酮	10.77	Isooctane 異辛烷	0.02
Isopropyl Alcohol 異丙醇	1.56	Mineral Oil, light 礦物油,輕	0.35
Bleach, ~5 % NaOCl 漂白劑, ~5% NaOCl	0.65	Mineral Oil, heavy 礦物油,重	0.27
Butyl Acetate 乙酸丁酯	0.84	Salt Water (3.5 % NaCl) 鹽水	0.64
Diesel 柴油	0.08	Sodium hydroxide (0.025 %, pH = 10) 氫氧化鈉	0.72
Diethyl glycol monomethyl ether 乙二醇單甲醚	2.38	Hydrogen Peroxide (3 %) 過氧化氫	0.75
Hydrolic Oil 液壓油	0.16	Xylene 二甲苯	0.42
Skydrol 5 航空液壓油	0.54	Strong Acid (HCI Conc) 強酸	8.21

註：1 x 1 x 1 cm 立方體在下列溶劑浸泡後24小時的重量增加百分比

Form2 樹脂與列印層厚度選擇	0.3 mm	0.14 mm	0.1 mm	0.05 mm	0.025 mm
一般樹脂透明 Clear			V	V	V
一般樹脂白色 White			V	V
一般樹脂灰色 Grey			V	V	V
一般樹脂黑色 Black			V	V	V
快速樹脂 Draft	V
高韌性樹脂 Tough			V	V
類PP樹脂 Durable			V	V
灰色Pro.樹脂 Grey Pro			V	V
彩色套件 Color Kit			V	V	V
彈性樹脂 Flexible			V	V
耐高溫樹脂 High Temp			V	V	V
精密牙模樹脂 Dental Model		V	V	V	V
高強度樹脂 Rigid			V	V
柔性樹脂 Elastic			V
可鑄用樹脂 Castable			V	V	V
精密蠟模樹脂 Castable Wax				V	V
牙科 SG 樹脂 Dental SG			V	V
牙科 LT 樹脂 Dental LT Clear			V

Formlabs Grey Pro Resin

Grey Pro Resin

Production Description

Features

Grey Pro Resin 1L

Full Line of Formlabs Resins